XPS study of interface formation of CVD SiO2 on InSb

The interfacial chemistry of CVD SiO2 films deposited on thin native oxides grown on InSb substrates is examined using X-ray photoemission spectroscopy (XPS) and a relatively benign chemical etching technique for depth profiling. An intensity analysis of XPS spectra is used to derive the compositional structure of the interfaces obtained in the SiO2/native oxide/InSb system. Peak positions in these spectra are used to follow the change in substrate surface potential during the etch sequence, and to establish the chemical nature of the species formed during deposition and subsequent processing. Reaction of the substrate with oxygen resulted in an In-rich native oxide and 1-2 monolayers of excess elemental Sb at the native-oxide/substrate interface, incompletely oxidized silane reduced the native oxide, leaving less than 1 monolayer of elemental In at the SiO2/native oxide interface. Etch removal of this thin In-rich layer leads to a change in the substrate surface potential of 0.06 eV, corresponding to a net increase in positive charge. The results are consistent with simple thermodynamic considerations; they are also compared to previously reported studies of deposited dielectrics on III-V compound semiconductors.