Mechanical properties of low tantalum alloys

The mechanical property behavior of equiaxed cast B-1900 + Hf alloy as a function of tantalum content was studied. Tensile and stress rupture characterization was conducted on cast to size test bars containing tantalum at the 4.3% (standard level), 2.2% and 0% levels. Casting parameters were selected to duplicate conditions used to prepare test specimens for master metal heat qualification. The mechanical property results as well as results of microstructural/phase analysis of failed test bars are presented.