Solidification of hypermonotectic Al-In alloys under microgravity conditions

Four samples of the Al-In system having monotectic and hypermonotectic compositions that were solidified under microgravity during the NASA-SPAR IX flight of January 20, 1981, are considered. The experimental thermal and physicochemical conditions that were actually achieved are analyzed. Radiographic and metallographic observations of the samples reveal a nonregular dispersed primary phase inside the monotectic matrix. These observations are discussed in relation to capillarity and solidification aspects. A key finding is the preservation of a certain degree of dispersion of the indium primary phase. This result differs fundamentally from the results obtained under microgravity conditions on the same system and compositions (Gelles and Markworth, 1980; Alborn and Loehberg, 1979). The results are seen as clearly establishing that the space environment can be used to obtain dispersed structures from hypermonotectic alloys.