Edge crack growth of thermally aged graphite/polyimide composites

Laminates of Celion 6000/LARC-160 and Celion 6000/PMR-15 graphite/polyimide composite materials were aged in air at temperatures of 202, 232, 260 and 288 C for various times up to 15,000 hours. Three unidirectional specimen types were studied: short beam shear (SBS), flexure, and 153 mm square panels. The interior region of the square panels exhibited little or no property degradation, whereas both laminate materials degraded and cracked preferentially at the specimen edge perpendicular to the fibers. Using a dye penetrant, the specimens were X-rayed and the crack depth measured as a function of time and temperature. A time temperature superposition of the crack data was successfully performed using an Arrhenius form for the shift factor. A direct correlation was found for edge crack depth and SBS strength for the LARC-160 laminates but the correlation for PMR-15 laminates was more complex.