Variation of Resin Properties Through the Thickness of Cured Samples

It is the purpose of this work to gain knowledge of the glassy materials used as matrices in composites and to study the homogeneity resulting from the curing process. An attempt is made to link the glass transition quantitatively with the presence of a given material. Expoxy resins containing various amounts of hardener (TGDDM/DDS system) were cured in a muffle furnace at 473 K for seven hours. The glass transition temperature, T sub g versus weight minus percent of hardener in the epoxy resin were measured. A limit was rapidly reached in T sub g at only two percent hardener. Thus, the glass transition of the fully cured epoxy-amine matrix seems not much different from the epoxide-epoxide cure. The T sub g versus cure-time for the epoxide-epoxide reaction was also studied. My 720 was cured by itself in an oil bath at 473 K for different lengths of time. The T sub g was found to increase exponentially with the cure time, and a maximum T sub g of about 450 K was reached after eleven hours. The reaction was found to be inhibited by running the sample under argon.