Characterization of Mode I and mixed-mode delamination growth in T300/5208 graphite/epoxy

The roles played by Mode I and Mode II strain-energy release rates (G-I and G-II, respectively) in inducing delamination growth under static and fatigue loading were investigated, using T300/5208 graphite/epoxy specimens. Double cantilever beam (DCB) specimens and cracked lap shear (CLS) specimens were used for pure Mode I and mixed-mode tests, respectively. Fatigue-induced delamination growth was characterized by constant-amplitude fatigue tests at a minimum to maximum cyclic load ratio of 0.05 and a frequency of 10 Hz. During the tests, the maximum and minimum strain-energy release rates (Gmax, Gmin) and the delamination growth rate (da/dN) were monitored. Static tests on mixed-mode CLS specimens measured the total strain-energy release rate, which was broken into G-I and G-II components using finite-element analysis. A power-law relationship between da/dN and G-Imax, and da/dN and Gmax were obtained from fatigue test results on DCB and CLS specimens, respectively. The power law for a pure Mode II delamination was derived from CLS results by subtracting the contribution due to G-I.