The characteristics of gamma-prime dislocation pairs in a nickel-base superalloy

The gamma-prime dislocation pairs of a single crystal nickel-base superalloy, PWA 1480, after tensile and fatigue loading at 650 C are analyzed. The existence and extent of cube cross slip in octahedral slip, and the nature of gamma-prime dislocation pairs in primary cube slip are investigated. It is observed that the PWA 1480 specimens oriented near (001) and (-3 6 10) line directions deform by octahedral slip and specimens oriented near (-1 1 1) and (-2 3 4) lines deform by primary cube slip. It is determined that the overall dislocation distributions are more homogeneous in low cycle fatigue (LCF) loading than in monotonic tensile loading; however, the gamma-prime dislocation pair characteristics are similar for tensile and LCF test specimens. The data reveal that the gamma-prime dislocation pairs of octahedral slip specimens are near-screw and on the cube cross slip plane and for the cube slip specimens, the dislocation pairs are of various characters and on the primary cube slip plane.