Thermal expansion of selected graphite-reinforced polyimide-, epoxy-, and glass-matrix composites

The thermal expansion of continuous carbon-fiber reinforced composites with epoxy-, polyimide-, and borosilicate glass-matrices has been measured and compared. The expansion of a rubber-toughened epoxy-matrix/P75S carbon-fiber composite was very different from the expansion of two different single-phase epoxy-matrix/P75S composites, although all three had the same stacking sequence. Reasonable agreement was obtained between measured thermal expansion data and results from classical laminate theory. Microdamage in the graphite/polyimide laminate, induced by 250 cycles between -156 and 121 C, caused a 53 percent decrease in the coefficient of thermal expansion. The thermal expansion of the graphite/glass laminate was not changed after 100 thermal cycles from -129 to 38 C; however, a residual strain of about 10 x 10 to the -6 was observed for the laminate tested.