Molten-salt corrosion of silicon nitride. I - Sodium carbonate. II - Sodium sulfate

An experimental study of the corrosion of Si3N4 under thin films of Na2CO3 at 1000 C has been conducted using both pure Si3N4 and Si3N4 with various additives. The reaction mechanism is shown to consist of: (1) the decomposition of Na2CO3 and the formation of Na2SiO3; (2) rapid oxidation; and (3) the formation of a protective silica layer below the silicate. In the second part, the corrosion mechanism of Si3N4 + Na2SO4/O2 at 1000 C was studied for both pure and additive-containing Si3N4. The reaction of Si3N4 + Na2SO4 was found to involve an initial period of slow weight loss (due to Na2SO4 vaporization and oxidation-dissolution) followed by further oxidation or the near termination of the reaction, depending on the Si3N4 additive.