Application of the V(R) resistance curve method to fracture of various crack configurations

The fracture resistance curve method of Newman (1985), based on the crack-tip-opening displacement, V(R), for a 'stationary' crack, was applied to various crack configurations in 2024-T351 and 7075-T651 aluminum alloys tested at room temperature. Using a stationary crack solution, the crack-tip-displacement was calculated at the current crack length for the crack configurations which included compact, middle-crack, single-edge-crack, and three-hole-crack tension specimens. The results showed that the V(R) resistance curves are insensitive to crack length, specimen width, and specimen type up to maximum load. After the maximum load is reached, the V(R) remains nearly constant; this constant depends only on specimen type, specimen width, and crack length. The V(R) resistance curve method can be used with the strip-yield analyses to accurately predict stable crack growth and instability of cracked metallic materials.