The influence of crack closure on fatigue crack growth thresholds in 2024-T3 aluminum alloyCrack opening loads were determined in load-shedding fatigue crack growth threshold tests on 2024-T3 aluminum alloy at stress ratios R of -2, -1, 0, 0.33, 0.5, and 0.7. The effects of load-shedding procedure and rate were investigated. Values of threshold Delta-K were found to vary significantly with R, whereas values of threshold effective Delta-K did not. That is, the variation of threshold Delta-K with R was almost completely explained by accounting for the measured variation in crack opening load behavior with R. The load-shedding guidelines of ASTM Test Method for Measurement of Fatigue Crack Growth (E 647) produced a threshold Delta-K value for R = 0.7 that was in agreement with the value determined using a procedure that should minimize closure effects. At both R = 0 and R = 0.7, high load-shedding rates produced high values of threshold Delta-K caused by large closure effects.
Document ID
19890030057
Acquisition Source
Legacy CDMS
Document Type
Conference Proceedings
Authors
Phillips, Edward P. (NASA Langley Research Center Hampton, VA, United States)