Simulated impact damage in a thick graphite/epoxy laminate using spherical indenters

The extent of fiber damage due to low-velocity impacts was determined for very thick graphite/epoxy laminates. The impacts were simulated by pressing spherical indenters against the laminates. After the forces were applied, the laminate was cut into smaller pieces so that each piece contained a test site. Then the pieces were deplied and the individual plies were examined to determine the extent of fiber damage. Broken fibers were found in the outer layers directly beneath the contact site. The locus of broken fibers resembled cracks. The cracks were more or less oriented in the direction of the fibers in the contiguous layers. The maximum length and depth of the cracks increased with increasing contact pressure and indenter diameter. The length and depth of the cracks were also predicted using maximum compression and shear stress criteria. The internal stresses were calculated using Hertz's law and Love's solution for pressure applied on part of the boundary of a semi-infinite body. The predictions and measurements were in good agreement.