Mechanical properties characterization of composite sandwich materials intended for space antenna applications

The composite materials proposed for use in the Advanced Communications Technology Satellite (ACTS) program contains a new, high modulus graphite fiber as the reinforcement. A study was conducted to measure certain mechanical properties of the new fiber-reinforced material as well as of a composite-faced aluminum honeycomb sandwich structure. Properties were measured at -157, 22, and 121 C. Complete characterization of this material was not intended. Longitudinal tensile, picture-frame shear, short-beam shear, and flexural tests were performed on specimens of the composite face-sheet materials. Unidirectional, cross-plied, and quasi-isotropic fiber composite ply layup designs were fabricated and tested. These designs had been studied by using NASA's Integrated Composite Analyzer (ICAN) computer program. Flexural tests were conducted on (+/- 60/0 deg) sub s composite-faced sandwich structure material. Resistance strain gages were used to measure strains in the tensile, picture-frame, and sandwich flexural tests. The sandwich flexural strength was limited by the core strength at 157 and 22 c. The adhesive bond strength was the limiting factor at 121 C. Adhesive mechanical properties are reflected in sandwich structure flexural properties when the span-to-depth ratio is great enough to allow a significant shear effect on the load-deflection behavior of the sandwich beam. Most measured properties agreed satisfactorily with the properties predicted by ICAN.