Room temperature tensile ductility in polycrystalline B2 Ni-30Al-20Fe

A room-temperature tensile elongation of about 2.5 percent, where the only slip vector observed was the 100, has been determined for a double-extruded B2 Ni-30Al-20Fe alloy consisting of recrystallized equiaxed grains about 25 microns in diameter; these results suggest that 100-slip does not preclude limited ductility in polycrystalline B2 alloys in tension at low temperatures. A suppression of ordering through resort to rapid solidification, in other words, is not necessary for ductility, since the cast and as-extruded alloy presently examined is ordered.