TEM studies of oxidized NiAl and Ni3Al cross sections

Cross sections of oxide scale/(Ni-Al) intermetallics were prepared by a new method and studied using primarily TEM. The cross sections were prepared by encasing an oxidized metal specimen sandwich in a low-melting-temperature zinc alloy. Observations of oxidized zirconium-doped beta-NiAl cross sections revealed crystallographic voids beneath an adherent Al2O3 scale. The oxide-metal interface was incoherent, but a high dislocation density in the metal near the interface suggested that a large tensile stress was induced by the attached oxide scale. A duplex Al2O3-NiAl2O4 scale formed on zirconium-doped and zirconium/boron-doped gamma-prime-Ni3Al alloys. Additional results are presented involving oxidation mechanisms and oxide-metal interface structures.