Response of notched AS4/PEEK laminates to tension/compression loading

Fatigue life, damage-initiation and propagation, and residual strength data are presently examined to ascertain the response of notched AS4/PEEK specimens to fully reversed tension/compression loading. Stiffness measurements made during the low-level fatigue history show that compression stiffness and tension stiffness degrade throughout the fatigue life. Damage to specimens fatigued at higher cyclic stresses developed primarily in the direction perpendicular to the loading. As in the case of specimens fatigued at lower stress levels, residual compressive stress decreased with damage development.