Gravimetric measurements of materials outgassing applied to graphite-epoxy laminates

The outgassing rates of two graphite-epoxy laminates, American Cyanamide 985B-626 and HST-7B-112, were obtained using a gravimetric method. The rates as a function of time and temperature were derived from the measurements of their mass losses at temperatures varying from 25 to 150 C and for a time span of up to 400 hours in a vacuum. The data from those measurements were reduced to obtain the outgassing activation energies, the mass losses per unit mass or area, and the corresponding outgassing rates. The rates are expressed in closed-form equations and are directly usable for modeling computations. The procedures to obtain these parameters are shown and may be used for the evaluation of other materials. The results of the tests show that the activation energies of the two materials are: 4630 cal/mole for the 985B-626 materials and 4791 cal/mole for the HST-7B-112 sample no. 10 Graphite Epoxy. The outgassing rates of these materials are in the 1OE-5 g sq cm/hr range and they decay according to a power of time of 0.60 at 25 C, indicating that the outgassing process is mainly a diffusion at that temperature. The normalized mass losses versus time obtained from these tests were compared to the discrete results obtained from the ASTM-E595 tests. The comparison provides general indications on the effects of temperature and time in relation to the ASTM test values obtained at 125 C for a 24-hour test duration.