Effect of Zn additions on precipitation during aging of alloy 8090

Precipitation events have been observed by TEM under two different aging conditions in three 'stretched' alloys, whose compositions are encompassed by the 8090 composition window but contain Zn additions of up to 1.07 wt pct. DSC was also used to obtain deeper insight of the precipitation-event effects obtainable through Zn content variation; it was thereby revealed that Zn is incorporated into the delta-prime phase, perhaps stabilizing it. Coarse, Zn-containing precipitates can form on the boundaries and within the interiors of the grains, when the Zn content reaches the presently investigated maximum of 1.07 wt pct.