Constitution of pseudobinary hypoeutectic beta-NiAl + alpha-V alloys

The formation of pseudobinary eutectics between NiAl (beta) and V (alpha) at high temperatures was investigated as a possible way of improving the ductility and toughness of the alloy. It is found that a pseudobinary eutectic, characterized by a large beta+alpha field, is formed in the Ni-Al-V ternary system below about 1370 C. The high-temperature solubility of V in beta is about 14 percent, decreasing markedly with decreasing temperature and increasing Al content above 50 at. pct Al. The pseudobinary hypoeutectic exibits crack resistance under indentation loading.