Preliminary studies on NiAl/Nb2Be17 reaction and effectiveness of BeO as an interfacial reaction barrier

The interfacial reaction between NiAl and Nb2Be17 (used as a reinforcement for the alloy) was studied by measuring diffusion bonding of NiAl and Nb2Be17 plates in a hot press under a vacuum of 10 exp -5 atm. It was found that, after 2 hrs of hot pressing at 1373 K, the reaction between NiAl and Nb2Be17 was extensive. A 40 to 50-micron-thick reaction zone consisted of three distinct layers at the NiAl/Nb2Be17 interface: layer A next to Nb2Be17, layer B in the middle, and layer C next to NiAl. Results of analysis of the reaction layers using energy dispersive spectroscopy (EDS) were inconclusive because of the inabiliaty of EDS to detect Be.