Spacecraft thermal control coatings

The Experiment AO 138-6 was located on the trailing edge of the Long Duration Exposure Facility as part of the French Cooperative Payload (FRECOPA) Experiment. It was purely passive in nature: material specimens 2 x 2 cm, independently mounted in sample-holders, with their surface in the same reference plane, were exposed to space. Thirty samples were set in a vacuum-tight canister which was opened in space a few days after LDEF deployment and closed while still in orbit ten months later; twenty-four samples were directly exposed to space for the total flight duration (preflight handling, shuttle bay environment, separation from shuttle, shuttle environment, LEO environment, docking, descent, transfer to KSC). Materials included paints (conductive or nonconductive), SSM's, polymeric films, surface coatings, composite materials, and metals. After sample retrieving, inspection and measurements were carried out in atmospheric laboratory conditions on each sample: observation with binocular lenses and scanning electron microscopy, spectral relectance and transmittance using an integrating sphere in the wavelength range 280-2300 nm, emissivity by the means of a Gier & Dunkle portable reflectometer, electron spectroscopy for chemical analysis-x-ray photoelectron spectroscopy (ESCA-XPS), and Rutherford backscattering spectroscopy (RBS) measurements on some selected samples. The results obtained from flight were compared to laboratory data obtained in UV-irradiation tests when these data were available. As a general statement a good spectral concordance is observed for all samples not in the canister so long as air recoveries are taken into account. For one material, the degradation is more important for the sample in the canister than for those of the same material mounted at the surface of the tray; for most samples in the canister the degradation is slightly higher than the one which can be predicted from laboratory standard irradiations. Contamination problems having been ruled out, the higher temperature experience by the samples on the inside of canister probably explains these phenomena.