Chemical stability of titanium diboride reinforcement in nickel aluminide matrices

Chemical stability of TiB2 reinforcement in NiAl (45 at percent Al) and Ni3Al (24 at percent Al) matrices has been theoretically and experimentally investigated. Calculations were made using thermodynamic properties of the systems to predict behavior at temperatures between 1173 and 1573 K. Experimental investigation of hot-press consolidated TiB2 particulate/prealloyed matrix powder blends were conducted using energy dispersive X-ray analysis, XRD, AES, and TEM. The theoretical and experimental analyses suggest that TiB2 is chemically stable in both matrices up to 1573 K; however, TiB2 was found to be less active in NiAl than in Ni3Al due to lower nickel activity in NiAl.