Mechanics of Granular Materials (MGM) Microgravity Experiment

The second series of MGM experiment was conducted during the STS-89 mission in January 1998. The experiment was previously flow on Atlantis's STS-79 mission in September 1996. Six displacement-controlled, drained triaxial compression experiments were performed at very low effective confining stresses. The confining stresses were in the ranges 0.05, 0.52 and 1.30 kPa. Three experiments were subjected to monotonic loading and unloading cycles while the other three experiments were subjected to cyclic loading. The results show very high peak strength friction angles in the range of 47.6 to 70.0 degrees, which are mainly due to overconsolidation and grain interlocking effects. It was observed that the residual strength levels in the monotonic loading experiments were in the same range as that observed at higher confining stress levels. The dilatancy angles were unusually high in the range of 30 to 31 degrees. All specimens display substantial initial stiffnesses and elastic moduli during unloading and reloading events, which are nearly an order of magnitude higher than conventional theories predict. A periodic instability phenomenon which appears to result from buckling of multiple internal arches and columnar systems, augmented by stick-slips was observed in the experiments. Computed Tomography (CT) measurements revealed valuable data about the internal fabric and the specimens deformation patterns. Uniform diffuse bifurcation with multiple radial shear bands was observed in the specimens tested in a microgravity environment. In the axial direction, two major conical surfaces were developed. Spatial nonsymmetrical deformations were observed in specimens tested in terrestrial laboratory.