Phenylethynyl Containing Polyarylene Ethers/Polyimides Resin Infiltration of CompositesThe following tasks were performed at NCA&TSU during the second year in performance of the grant. LaRC-LV-1 13 resin was synthesized at NCA&TSU. In order to perform the synthesis, glassware and needed apparatus were purchased with grant funds along with the appropriate monomers. It was found that the LaRC-LV-1 13 resin was easily synthesized by the NMP solvent/toluene imminization/distilled water precipitation process. However, in use this resin exhibited a bubbling/foaming behavior during cure that was detrimental leading to the production of composite panels having a high void content. Composite panels were fabricated using compression molding and resin transfer molding (RTM) techniques. Initial fiber volume determinations were computed at NCA&TSU along with NASA-Langley measured c-scans on the panels produced. The initial results indicated a unsatisfactory level of approximately 20% by volume of voids. Testing of uniaxial coupons in compression to failure also agreed with these results. The uniaxial coupons delaminated as the major mode of failure indicative of an unacceptably low level of resin and to much void content in the final composites produced. In discussions with Dr. Brian Jensen, it was suggested the void fraction needs to be reduced to at least 2% by volume for a useful composite. The panels produced used both resin synthesized at NASA-Langley and NCA&TSU. In reviewing our progress over the past year, it was noted that the resin as formulated by the current synthesis process bubbled at elevated temperature. This was especially observed in neat resin slugs cured at the recommended one, four and eight hour cure temperatures. Pressurized cures where then performed with pressures up to 200 psi and simultaneously the lowest eight hour cure temperatures. Although this procedure reduced the amount of bubbles to some extent in the neat resin slugs it did not completely eliminate them. The cure reaction appears to be very energetic even at the lowest recommended cure temperature. Currently, the pressurized cure apparatus developed at NCA&TSU is limited to 200 psi.
Document ID
20000021548
Acquisition Source
Langley Research Center
Document Type
Other
Authors
Dunn, DeRome O.
(North Carolina Agricultural and Technical State Univ. Greensboro, NC United States)
Date Acquired
August 19, 2013
Publication Date
October 12, 1998
Subject Category
Nonmetallic Materials
Funding Number(s)
CONTRACT_GRANT: NAG1-1874
Distribution Limits
Public
Copyright
Work of the US Gov. Public Use Permitted.
Document Inquiry

Available Downloads

There are no available downloads for this record.
No Preview Available