Characterization of a Structural Transformation of Carbon Nanotube Materials by Raman Spectroscopy

Raman spectra of carbon nanotubes and carbon microstructure materials synthesized on Si substrates by pulsed laser vaporization have been measured in the range of 50/cm to 4500/cm with the excitation of He-Ne laser. It is found that the formation of nanotubes depends strongly on the growth temperatures and high quality multi-wall and single-wall nanotubes were produced at 700 and 990 C, respectively. The Raman spectra of one sample grown at 700 C were found to be dependent on the excitation intensity. The spectra of the sample suggest that the structure is similar to that of multi-wall nanotubes at low excitation intensity (2.5 kW/sq cm) and it converts to the structure of single-wall nanotubes at higher intensity (25 kW/sq cm). Measurements taken while cycling the light intensity indicate a reversible structural transition.