Thermostructural Analysis of Carbon Cloth Phenolics "Ply Lifting" and Correlation to LHMEL Test Results

This paper provides a discussion of the history of Carbon Cloth Phenolic (CCP) ply lifting in the Redesigned Solid Rocket Motor (RSRM) Program, a brief presentation of theoretical methods used for analytical evaluation, and results of parametric analyses of CCP material subject to test conditions of the Laser Hardened Material Evaluation Laboratory. CCP ply lift can occur in regions of the RSRM nozzle where ply angle to flame surface is generally less than about 20 degrees. There is a heat rate dependence on likelihood and severity of the condition with the higher heating rates generally producing more ply lift. The event occurs in-depth, near the heated surface, where the load necessary to mechanically separate the CCP plies is produced by the initial stages of pyrolysis gas generation due to the thermal decomposition of the phenolic resin matrix. Due to the shallow lay-up angle of the composite, normal components of the indepth mechanical load, due to "pore pressure", are imparted primarily as a cross-ply tensile force on the interlaminar ply boundaries. Tensile capability in the cross-ply (out of plane) direction is solely determined by the matrix material capability. The elevated temperature matrix material capabilities are overcome by pressure induced mechanical normal stress and ply-lift occurs. A theoretical model used for CCP in-depth temperature, pressure, and normal stress prediction, based on first principles, is briefly discussed followed by a parametric evaluation of response variables subject to boundary conditions typical of on-going test programs at the LHMEL facility. Model response demonstrates general trends observed in test and provides insight into the interactivity of material properties and constitutive relationships.