Developing Glassy Magnets from Simulated Composition of Martian Soil for Exploration Applications

The long-term exploration goals of NASA include developing human habitation on Mars and conducting scientific investigations on Mars and other planetary bodies. In situ resource processing is a key objective in this area We focus OR the possibility of making magnetic glasses in situ for potential applications development. The paper will focus on ongoing work at NASA Marshall Space Flight Center on making magnetic glass h m Mars soil simulants and its characterization. Analysis of the glass morphology, strength, chemistry and resulting magnetic properties will provide a fi.mdamenta1 understanding ofthe synthesized materiai that can be used for pomtiai appiications cieveiopment. In an effort to characterize the magnetic properbes of the Mars glasses, a series of tests were performed at NASA MSFC. Preliminary tests indicated that the glasses were attracted to a magnet and also had a small amount of residual magnetism. They were opaque (almost black in color). As the first step, a sample of Mars 1 glass (-lm x lmm x 5 mm length) was machined, weighed and its hysteresis curve was measured using a Vibration Sample Magnetometer 0. Next, a small furnace was designed and built and the sample was baked in a graphite (reducing agent) crucible at 800 C in an Argon atmosphere for 3 hours in the presence of a uniform, transverse (transverse to the 5mm length of the sample) magnetic field of 0.37 Tesla. The treated sample showed reddening on the outside and showed substantially increased residual magnetism. This sample was again analyzed in the VSM. The data clearly showed that some chemical change occurred during the heat treatment (color change) and that both the glasses have useful magnetic properties. Although no orientation effects of the magnetic field were considered, the data showed the following: 1. Both glass samples are primarily soft magnets and display ferromagnetic behavior (hysteresis, saturation, etc.) 2. The treated glass has improved saturation magnetism (order of magnitude increase), retentivity (factor of 6 increase) and susceptibility (order of magnitude increase) compared to the untreated glass 3. The untreated sample has higher coercivity (-50% that of Nickel) than the treated sample