Effects of heat treating PM Rene' 95 slightly below the gamma' solvus

An investigation was performed on as-hot-isostatically-pressed (As-HIP) Rene' 95 to obtain additional information on the variation of the amount of gamma prime with solutioning temperatures near the gamma prime solvus temperature and the resulting effects on tensile and stress rupture strength of As-HIP Rene' 95. The amount of gamma prime phase was found to increase at a rate of about 0.5% per degree Celsius as the temperature decreased from the solvus temperature to about 50 C below the gamma prime solvus temperature. The change in the amount of gamma prime phase with decreasing solutioning temperature was observed to be primarily associated with decreasing solubilities of Al+Ti+Nb and increasing solubility of Cr in the gamma phase.