Compression strength failure mechanisms in unidirectional composite laminates containing a hole

Experiments on graphite-epoxy laminated plates containing unloaded small holes show that these laminates are notch insensitive. That is, the uniaxial strength of these laminates with small holes exceeds the strength predicted by a point stress criterion using the stress concentration factor for the in-plane stress field. Laminates containing large holes exhibit notch sensitive behavior and consequently their strength is reasonably well predicted by the stress concentration effect. This hole size effect is manifested both in tension and in compression. Apparently, some mechanism must cause in-plane stress relief for laminates containing small holes. The purpose of this research was to study the influence of geometric nonlinearity on the micromechanical response of a filamentary composite material in the presence of a strain gradient caused by a discontinuity such as a hole. A mathematical model was developed at the micromechanical level to investigate this geometrically nonlinear effect.