Validity Using Pump-Probe Pulses to Determine the Optical Response of Niobate Crystals

A variety of niobate crystals have found their places in nonlinear optical applications as well as in laser devices. In recent years much attention has been paid to study the ultrafast optical response in a variety of photorefractive crystals such as KTa(1-x)Nb(x)O3 and KNbO3 crystals, glasses, semiconductors and polymers for applications in optical switching, information processing, optical computing, and all-optical device systems. Third-order optical nonlinearity is the most important property for realization of all-optical switching. Therefore experiments have been performed on the third order susceptibility using a variety of techniques such as the third-order harmonic generation, EFISH and degenerate four-wave mixing(DFWM). The latter has been conducted with a variety of pump wavelengths and with nanosecond, picosecond and femtosecond pulses. Niobate crystals, such as potassium niobate KNbO3, potassium tantalate niobate KTN family (KTa(1-x)Nb(x)O3), strontium barium niobate SBN (Sr(x)Ba(1-x)Nb2O6) and potassium-sodium niobate SBN (KNSBN) are attractive due to their photorefractive properties for application in optical storage and processing. The pulsed probe experiments performed on theses materials have suggested two types of time responses. These responses have been associated with an coherent response due to Chi(sup 3), and a long lived component due to excited state population. Recent study of DFWM on KNbO3 and KTN family reveals that the long lived component of those crystals depends on the crystal orientation. A slowly decaying signal is observable when the grating vector K(sub g) is not perpendicular to the C-axis of those photorefractive crystals', otherwise the optical response signal would be only a narrow coherent peak with FWHM equal to the cross-correlation width of the write beam pulses. Based on this understanding, we study the photodynamical process of a variety of niobate crystals using DFWM in a Kg perpindicular to C geometry with a ps-YAG: Nd laser operating at 532nm. However, the discrepancies in numerical estimations of Chi(sup 3) in these materials and other nonlinear optical media have resulted in a number of discussions. In order to better understand the photodynamical process of niobate crystals after an short pulse excitation we analyze the factors governing the coherent signal and present the DFWM spectra of niobate crystals.