Buckling and Failure Tests of a Subscale Composite Cylinder

A subscale solid laminate composite cylinder 31.5-in. diameter and 47.8 in. long with a [23/0/-23]4S layup known as NDL-1 was designed to fail in buckling and tested in axial compression to collapse twice. The proposed paper will focus on comparing the behavior of NDL-1 from the first test to failure (TTF-1) and the second test to failure (TTF-2). NDL-1 had a peak load of 466.3 kips during TTF-1 and a peak load of 390.4 kips, 15.5% lower, but with a similar stiffness, during TTF-2. Failure initiated at the 200º circumferential location in TTF-1, and at the 30º circumferential location in TTF-2. Though failure initiated at different locations, a similar radial deformation pattern was present just prior to collapse in TTF-1 and TTF-2. A shallow delamination occurred due to the initial failure event in TTF-1, and the damage had no influence on the response of NDL-1 during TTF-2. In the end, it was determined that NDL-1 failed in buckling during TTF-1 and TTF-2, and the second test to failure of NDL-1 highlighted interesting observations with respect to the effect of damage.