Characterization of Composite Damage Using Passive Thermography

Passive thermography is used to monitor small increases in temperature on a composite structure during loading. A rise in temperature can be attributed to damage formation due to matrix cracking and fiber breaks. An infrared camera allows for imaging the damage location, size, and shape. Recently, a technique has been developed to estimate the depth of the damage in a composite hat-stiffened panel during quasi-static loading. This technique is based on two heat generation components. The first component is an instantaneous thermoelastic response due to a strain release. The second component is mechanical heating, at the interface of failure, due to fracture damage. This second component produces a transient rise in temperature that is a function of the damage depth and thermal diffusivity. The first component defines the thermal start time for the transient response. A one-dimensional thermal model is used to determine the damage depth for a known thermal diffusivity. The results are compared to ultrasonic and X-ray CT data and show good agreement for damage depth.